Requisita ad Optical Color-Shifting Pigmenta pro Automotive Coatings.

Optical Color-Shifting Pigmentsquia Automotive CoatingsEst genus linteorum multi-strati sicut pigmenti quod significant transitum colorem patitur cum mutationibus in angulo observationis / luminis fons est angulus. nucleus in alterna ACERVUS ACERVORUM altae/low refractivae indicis structurarum (ut TiO₂/SiO₂/TiO₂) consistit, et densitas stratum intra nanometri tolerantiam moderari debet ut colori constantiam conservet.

Genus 1. structural

Media type (DOVP): stratum mediarum plenum (ut SiO₂ + TiO₂), diaphanum, aptum ad subiecta luce coloratum, colore splendido et bono tempestatis resistente.

Metallum reflexivum genus: nucleus metallicus (Al/Cr/Ag) + media strato, opaco, cum satietatem superior color.

Magnitudo particularis: Communiter 10-50 µm; Magnitudo tenuis particula (<15 µm) tenera est, dum grossa particula (25-50 µm) fortis splendor est.

Crassitudo: Singula scheda circa 1 µm, apta ad systemata membranarum tenuium pro autocinetis.

2. Optical euismod Requisita (Core)

Chromatic Change Effect (Goniochromism)

Multi-angulus Color differentiae valoris: E ≥ 15 (15° → 110°), Insignes Coloris / Multi-coloris Transitus (ut Viridis → Purpura, Aurum → Caeruleum).

Mensuratio Signa: ASTM E2539 (Interference Type), ASTM E2194 (Metal Type); Mensurae Anglorum: r15as15°, r15as45°, r15as110°.

Color constantia

Batch differentia coloris: ΔE ≤ 2.0; Uniformitas particulae magnitudo distributionis intra eandem massam: ≥ 99% (ISO 13320).

Claritas et claritas

Inlustratio summa (20° ≥ 90 GU), alta visio (DOI ≥ 85); directio gradus **≥ 95% (ASTM D5767)**, nulla plagarum / frosting.

3. Application et Compatibility Requisita

Ratio Accommodatio

Generale pro solvendo substructio / aqua substructio / pulveris tunicarum; ad systemata aquarum innixa, modificatio superficies (qualis SiO₂ efficiens) requiritur, ad impediendam gasi hydrogenii remissionem et floccationem.

Compatible cum polyurethane / acrylica / epoxy resinae; Commendatur condiciones sanandas: 120-160℃/20-30 minuta.

Dosis:

Summa solidorum contentorum: 1-5%; 1-2.5% pro normali effectu, 2.5-5% pro magno colore intensio.

Construction Requirements

Imbre viscositas: 18-25 secundis (pro 4 scyphis efficiens); Crassitudo pellicula: Tunica perspicua 30-50 µm + lorica 20-30 µm.

Electrostatica spargit convenientiam: Resistentia 10⁶-10⁹ Ω·cm, pulveris depositionis rate ≥ 85%.